Cold Drawn Chq Ml08al Drawn Wire Phospahte Coated Rivets Screws Nuts Annealed Fastener Steel Wire

Stainless steel screw cable can also be known as stainless steel cold forging cable, which is principally used for a variety of sorts of attachments, such as mechanical components and electronic application components.

Send Inquiry
Cold Drawn Chq Ml08al Drawn Wire Phospahte Coated Rivets Screws Nuts Annealed Fastener Steel Wire
We improve industrial concentration through industry restructuring and integration, actively promote smart manufacturing, and become a world-class provider of the Stainless Angle, 410s stainless steel sheets, 2205 stainless steel sheets. To nurture our heart with virtue and walk with the Way is the foundation of our struggle, and to create customer service value is our business philosophy. Welcome your enquiry, best service will be provided with full heart.

Product Description

Stainless steel screw cable can also be known as stainless steel cold forging cable, which is principally used for a variety of sorts of attachments, such as mechanical components and electronic application components. According to various materials, corresponding anti-corrosion and mechanical properties can be found. To be able to get a better formability during cold forging, higher quality is selected. Appropriate wire material is especially important.


Production Rang:

Size: Diameter 0.2mm-5.5mm, 5.5mm-12mm

Standard: GB1220, ASTM A484/484M, EN 10060/ DIN 1013 ASTM A276, EN 10278, DIN 671

Main Grade: 201, 304, 316, 316L, 310s, 430

Finish: Black, NO.1, mill finish, cold draw


Main grade description in different standard

ASTM

DIN / EN

JIS

GB

ISO Name

Other

S20100

201

1.4372

SUS201

S35350

X12CrMnNiN17–7-5

J1 L1 LH 201J1

S20200

202

1.4373

SUS202

S35450

X12CrMnNiN18–9-5

202 L4, 202 J4, 202 J3

S30400

304

1.4301

SUS304

S30408

X5CrNi18-10

06Cr19Ni10

0Cr18Ni9

S31603

316L

1.4404

SUS316L

S31603

X2CrNiMo17-12-2

022Cr17Ni12Mo2 00Cr17Ni14Mo2

S40900

409

-

SUH409

S11168

X5CrTi12

0Cr11Ti

S31008

310S

1.4951

SUS310S

S31008

X12CrNi23-12

06Cr25Ni20

0Cr25Ni20

S41008

410S

1.4000

SUS410S

S11306

X6Cr13

-

S43000

430

1.4016

SUS430

10Cr17

X6Cr17

1Cr17


Main grade chemical component in different standard

201

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.15

1.00

5.5-7.5

0.050

0.030

3.5-5.5

16.0-18.0

0.25

-

DIN/EN

0,15

1,00

5,5-7,5

0,045

0,015

3,5-5,5

16,0-18,0

0,05-0,25

-

JIS

0.15

1.00

5.5-7.5

0.060

0.030

3.5-5.5

16.0-18.0

0.25

-

GB

0.15

1.00

5.5-7.5

0.050

0.030

3.5-5.5

16.0-18.0

0.05-0.25

-

202

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.15

1.00

7.5-10.0

0.060

0.030

4.0-6.0

17.0-19.0

0.25

-

DIN/EN

0,15

1,00

7,5-10,5

0,045

0,015

4,0-6,0

17,0-19,0

0,05-0,25

-

JIS

0.15

1.00

7.5-10.0

0.060

0.030

4.0-6.0

17.0-19.0

0.25

-

GB

0.15

1.00

7.5-10.0

0.050

0.030

4.0-6.0

17.0-19.0

0.05-0.25

-

304

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.08

0.75

2.00

0.045

0.030

8.0 - 10.5

18.0-20.0

0.10

-

DIN/EN

0,07

1,00

2,00

0,045

0,015

8,0 - 10,5

17,5-19,5

0,10

-

JIS

0.08

1.00

2.00

0.045

0.030

8.0 - 10.5

18.0-20.0

-

-

GB

0.08

1.00

2.00

0.045

0.030

8.0 - 10.0

18.0-20. 0

-

-

316L

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.030

0.75

2.00

0.045

0.030

10.0-14.0

16.0-18.0

0.10

2.00-3.00

DIN/EN

0,030

1,00

2,00

0,045

0,015

10,0-13,0

16,5-18,5

0,10

2,00-2,50

JIS

0.030

1.00

2.00

0.045

0.030

12.0-15.0

16.0-18.0

-

2.00-3.00

GB

0.030

0.75

2.00

0.045

0.030

10.0-14.0

16.0-18.0

0.10

2.00-3.00

409

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Ti %

ASTM

0.08

1.00

1.00

0.045

0.03

0.50

10.5-11.7

-

6*C% - 0.75

DIN/EN

-

-

-

-

-

-

-

-

-

JIS

0.08

1.00

1.00

0.040

0.030

-

10.5-11.7

-

6*C% - 0.75

GB

0.08

1.00

1.00

0.045

0.030

0.60

10.5-11.7

-

6*C% - 0.75

310s

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.08

1.50

2.00

0.045

0.030

19.0-22.0

24.0-26.0

-

-

DIN/EN

0,10

1,50

2,00

0,045

0,015

19,0-22,0

24,0-26,0

0,10

-

JIS

0.08

1.50

2.00

0.045

0.030

19.0-22.0

24.0-26.0

-

-

GB

0.08

1.50

2.00

0.045

0.030

19.0-22.0

24.0-26.0

-

-

410S

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.08

1.00

1.00

0.040

0.030

0.60

11.5-13.5

-

-

DIN/EN

0,08

1,00

1,00

0,040

0,015

-

12,0-14,0

-

-

JIS

0.08

1.00

1.00

0.040

0.030

-

11.5-13.5

-

-

GB

0.08

1.00

1.00

0.040

0.030

0.60

11.5-13.5

-

-


Main grade mechanical property in different standard

201

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

260

515

40

-

95

217

-

JIS

275

520

40

241

100

-

253

GB

205

515

30

- 

99

-

- 

202

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

260

620

40

-

-

241

-

JIS

275

520

40

-

95

207

218

GB

-

-

-

-

-

-

-

304

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

205

515

40

-

92

201

-

JIS

205

520

40

187

90

-

200

GB

205

515

40

-

92

201

210

316L

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

170

485

40

-

95

217

-

JIS

175

480

40

187

90


200

GB

170

485

40

-

95

217

220

409

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

-

-

-

-

-

-

-

JIS

175

360

22

162

80

-

175

GB

-

-

-

-

-

-

-

310s

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

205

515

40

-

95

217

-

JIS

205

520

40

187

90

-

200

GB

205

515

40

-

95

217

220

410S

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

205

415

22

-

89

183

-

JIS

205

410

20

-

88

183

200

GB

205

415

20

-

89

183

200


Production Process

Good corrosion resistance and optimum formability.

Electronic components, high-rise curtain walls and building decoration fasteners.

301 stainless steel displays clear work hardening during deformation and is used in a variety of events requiring higher strength.


302 stainless steel is essentially a variant of 304 stainless steel with a higher carbon material, which is made to obtain increased durability through cold rolling.


302B is a type of stainless steel with high silicon content, it's high resistance to high temperature oxidation.


They're employed in events that need free cutting and higher surface gloss.

303Se stainless steel can be used to create parts that need hot bothering, because under these circumstances, this stainless steel has great hot workability.


304L is a version of 304 stainless steel with lower carbon content and can be used where welding is required. The lower carbon content reduces the precipitation of carbides in the heat-affected zone near the weld, and the precipitation of carbides can cause stainless steel to make intergranular corrosion (welding erosion) in particular surroundings.


316 (18Cr-12Ni-2.5Mo) material: because of the inclusion of Mo, its corrosion resistance, atmospheric corrosion resistance and high temperature strength are especially excellent. It may be used under harsh conditions; it's excellent work hardening (non-magnetic).


Stainless steel screw cable and stainless steel cold heading bai cable are usually manufactured from 304M, 304HC, and 316. They are currently among the most frequently used materials of 300 series austenitic stainless steel.


Application

The main customers are Germany BECK, EASE FORTUNE, Japan and South Korea market and domestic high-end market, with a global market share of over 50%.


The objective of stainless steel screw cable: the hardness of stainless steel screw wire makes them be used for different functions. They are usually used as little screws in everyday life, but also as automobile compression and screws screws, which are frequently utilised in normal life. Kinds of stainless steel screw wires: in look, screw wires are usually split into matte spring cord and glistening screw wire. The hardness of matte screw wire is higher than that of shiny twist wire. It can be utilized as a hanger cord. For goods with low appearance requirements and higher elasticity requirements. Papermaking, oxalic acid, fertilizer and other manufacturing equipment; photography, food industry, coastal area amenities, ropes, CD rods, bolts, nuts


We constantly strive to improve and innovate Cold Drawn Chq Ml08al Drawn Wire Phospahte Coated Rivets Screws Nuts Annealed Fastener Steel Wire, continuously improve our services and increase our users. We have established a talent management mechanism that selects on merit, makes the best use of talent, rewards and punishments, and provides compatible incentives. Our company always adhere to quality first, we serve our customers attentively and strive to improve our professional level. Satisfactory service and high-quality products are our unremitting pursuit and driving force.
Hot Tags: stainless steel wire screw, China, manufacturers, suppliers, factory, wholesale, buy, price, disturbutor, for sale, rivet wire, Stainless Sheet Metal, 304 stainless steel plate, 410 stainless steel plate, PVC Coated Stainless Pipe, stainless steel coil tubing
Related Showrooms
Leave Message
Your privacy is important to us - we never sell or share your information.