High Quality 304 201 Hairline Stainless Steel Plate
20-1 stainless steelhaving a acid and alkali resistance therefore forth, could be your creation of scenarios, back cover of materials. Utilized for pipe pipe, a few shallow drawing on solutions.
Send Inquiry
Product Description
20-1 stainless steelhaving a acid and alkali resistance therefore forth, could be your creation of scenarios, back cover of materials. Utilized for pipe pipe, a few shallow drawing on solutions.
1Cr17Mn6Ni5N, fresh grades: 12Cr17Mn6Ni5N 201C about the basis of both how 20-1 continue to Grades of steel, also as 201C, could be your progress of China's individual 201. Seemed that the Reduce material management of 200 Lower the content, boost the content. Mainly has the following 200 forms of steel grades: L1, LH, LA, L4, J1, J3, J4, Steel 20-1 forms of steel, and 20-1 national standard grades are: the older new China
Even the 200 series stainless steel has been manufactured at the United States being a replacement its 300 series stainless steel throughout World War II. As a result of war, Then, impeccable because a material was commanded by nations, and also also the distribution at the United States was inadequate. As a way to take care of the issue of distribution and this creation of stainless steel while inside lack of impeccable supply's instance of, '' the United States has generated a run of austenitic stainless steels predicated on impeccable.
Subsequent to the Ending of World War II, the Source of nickel at the United States Slowly Enhanced. The creation of 300 series stainless steel is restricted by the lack of materials, and therefore the 200-series have yet been further grown. Numerous Indians that have been engaged with the evolution of 200 series stainless steels came back into India. Beginning with the simple fact India is full of manganese funds and missing nickel tools, the 200 series stainless steel forms grown inside the United States is likely to undoubtedly be attracted into India.
Production Rang :
-201 Cold Rolled Stainless Steel Sheet and Plate , Cold rolled 201 sheet, Cold rolled 201 Plate
Thickness: 0.2mm - 3.0mm
Thickness: 3.0mm-8.0mm, special for cold rolled
Width: 300mm - 2000mm, the narrowed products pls check in strip products
Length: 1000mm-6000mm
Finish: 2B, 2D
-201 Hot Rolled Stainless Steel Sheet and Plate , Hot Rolled 201 Sheet, Hot Rolled 201 Plate,201 PMP, 201 CMP
Thickness: 1.2mm - 200mm
Width: 300mm - 3200mm
Length: 500mm – 12000mm
Finish: Black, NO.1, Anneal pickling
201 mechanical property in different standard
201 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 260 | 515 | 40 | - | 95 | 217 | - |
JIS | 275 | 520 | 40 | 241 | 100 | - | 253 |
GB | 205 | 515 | 30 | - | 99 | - | - |
Production Process and Feature
Simple Comparison about 201 and 304
Demands to select the best material. 304 stainless steel along with 20-1 stainless steel Rust, 20-1 can be useful for conditions isn't not as, or even significant Demanding on stainless steel, the price tag, 304 will be higher compared to purchase price tag on Gap: that the gist of the material recorded the compound on the gap 201, even as Stated by the usage of this surroundings, manufacturing The Item caliber 304, 20-1 is Utilised in surroundings that are complicated, Where powerful immunity to Article of the components of this material is different finished 304 functionality corrosion immunity Is Much Better compared to
Application
The use of 200 series stainless steel has been powerful in India on account of the prospect of replacement 304 stainless steel in certain software.