Free Samples 304 316 Stainless Steel Round Bar

Round bar is a general shape in the stainless steel industry, is a solid round bar with a circular section. Its specifications in diameter, usually expressed in millimeters (mm), such as "50mm" means that the diameter of 50mm round bar.

Send Inquiry
Free Samples 304 316 Stainless Steel Round Bar

We will comprehensively increase the pace of corporate internal restructuring, improve product innovation technology to create Industrial Stainless steel Pipe, Stainless Steel Rod, Duplex Stainless Steel that meet customer needs. Welcome new and old customers to visit and discuss, your demand is the source of our innovation, your support is the guarantee of our development. Customer satisfaction and success is our pursuit, we will make unremitting efforts to this end. We strive to improve operational efficiency in the process of procurement, production and marketing. We firmly believe that "your demand is our demand, your satisfaction is our responsibility". We adhere to the mission of 'making products intelligent and service intimate'.

Product Description

· Round bar is a general shape in the stainless steel industry, is a solid round bar with a circular section. Its specifications in diameter, usually expressed in millimeters (mm), such as "50mm" means that the diameter of 50mm round bar.

· Round Bar usually include 3 process way, hot-rolled, forged and cold-drawn t. Hot-rolled bar specifications for the 5.5-250 mm.

· Forged for more than 250mm diameter bar, cold drawn for below 50mmsize, 5.5-25 mm small round mostly straight bundles be supplied, and commonly used as steel, bolts and various mechanical parts; more than 25 mm of round steel, mainly for the manufacture of mechanical parts, seamless steel tube blank etc.


Production Rang :

Diameter: 3mm-480mm, 1/8" to 2 1/4"

Standard: GB1220, ASTM A484/484M, EN 10060/ DIN 1013 ASTM A276, EN 10278, DIN 671

Main Grade: 201, 304, 316, 316L, 310s, 430

Finish: Black, NO.1, mill finish, cold draw, H9, H11


Main grade description in different standard

ASTM

DIN / EN

JIS

GB

ISO Name

Other

S20100

201

1.4372

SUS201

S35350

X12CrMnNiN17–7-5

J1 L1 LH 201J1

S20200

202

1.4373

SUS202

S35450

X12CrMnNiN18–9-5

202 L4, 202 J4, 202 J3

S30400

304

1.4301

SUS304

S30408

X5CrNi18-10

06Cr19Ni10

0Cr18Ni9

S31603

316L

1.4404

SUS316L

S31603

X2CrNiMo17-12-2

022Cr17Ni12Mo2 00Cr17Ni14Mo2

S40900

409

-

SUH409

S11168

X5CrTi12

0Cr11Ti

S40910

409L

1.4512

SUH409L

S11163

X2CrTi12

00Cr11Ti

022Cr11Ti

S41008

410S

1.4000

SUS410S

S11306

X6Cr13

-

S43000

430

1.4016

SUS430

10Cr17

X6Cr17

1Cr17


Main grade chemical component in different standard

201

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.15

1.00

5.5-7.5

0.050

0.030

3.5-5.5

16.0-18.0

0.25

-

DIN/EN

0,15

1,00

5,5-7,5

0,045

0,015

3,5-5,5

16,0-18,0

0,05-0,25

-

JIS

0.15

1.00

5.5-7.5

0.060

0.030

3.5-5.5

16.0-18.0

0.25

-

GB

0.15

1.00

5.5-7.5

0.050

0.030

3.5-5.5

16.0-18.0

0.05-0.25

-

202

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.15

1.00

7.5-10.0

0.060

0.030

4.0-6.0

17.0-19.0

0.25

-

DIN/EN

0,15

1,00

7,5-10,5

0,045

0,015

4,0-6,0

17,0-19,0

0,05-0,25

-

JIS

0.15

1.00

7.5-10.0

0.060

0.030

4.0-6.0

17.0-19.0

0.25

-

GB

0.15

1.00

7.5-10.0

0.050

0.030

4.0-6.0

17.0-19.0

0.05-0.25

-

304

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.08

0.75

2.00

0.045

0.030

8.0 - 10.5

18.0-20.0

0.10

-

DIN/EN

0,07

1,00

2,00

0,045

0,015

8,0 - 10,5

17,5-19,5

0,10

-

JIS

0.08

1.00

2.00

0.045

0.030

8.0 - 10.5

18.0-20.0

-

-

GB

0.08

1.00

2.00

0.045

0.030

8.0 - 10.0

18.0-20. 0

-

-

316L

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.030

0.75

2.00

0.045

0.030

10.0-14.0

16.0-18.0

0.10

2.00-3.00

DIN/EN

0,030

1,00

2,00

0,045

0,015

10,0-13,0

16,5-18,5

0,10

2,00-2,50

JIS

0.030

1.00

2.00

0.045

0.030

12.0-15.0

16.0-18.0

-

2.00-3.00

GB

0.030

0.75

2.00

0.045

0.030

10.0-14.0

16.0-18.0

0.10

2.00-3.00

409

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Ti %

ASTM

0.08

1.00

1.00

0.045

0.03

0.50

10.5-11.7

-

6*C% - 0.75

DIN/EN

-

-

-

-

-

-

-

-

-

JIS

0.08

1.00

1.00

0.040

0.030

-

10.5-11.7

-

6*C% - 0.75

GB

0.08

1.00

1.00

0.045

0.030

0.60

10.5-11.7

-

6*C% - 0.75

409L

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Ti %

ASTM

0.03

1.00

1.00

0.040

0.020

0.50

10.5-11.7

0.03

6*(C+N)-0.5

DIN/EN

0.03

1.00

1.00

0.040

0.015

-

10.5-12.5

-

6*(C+N)-0.65

JIS

0.03

1.00

1.00

0.040

0.030

-

10.5-11.7

-

6*C% - 0.75

GB

0.03

1.00

1.00

0.040

0.020

-

10.5-11.7

0.03

Ti≥8*(C+N)

410S

C %

Si%

Mn %

P %

S %

Ni %

Cr %

N %

Mo %

ASTM

0.08

1.00

1.00

0.040

0.030

0.60

11.5-13.5

-

-

DIN/EN

0,08

1,00

1,00

0,040

0,015

-

12,0-14,0

-

-

JIS

0.08

1.00

1.00

0.040

0.030

-

11.5-13.5

-

-

GB

0.08

1.00

1.00

0.040

0.030

0.60

11.5-13.5

-

-


Main grade mechanical property in different standard

201

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

260

515

40

-

95

217

-

JIS

275

520

40

241

100

-

253

GB

205

515

30

- 

99

-

- 

202

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

260

620

40

-

-

241

-

JIS

275

520

40

-

95

207

218

GB

-

-

-

-

-

-

-

304

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

205

515

40

-

92

201

-

JIS

205

520

40

187

90

-

200

GB

205

515

40

-

92

201

210

316L

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

170

485

40

-

95

217

-

JIS

175

480

40

187

90


200

GB

170

485

40

-

95

217

220

409

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

-

-

-

-

-

-

-

JIS

175

360

22

162

80

-

175

GB

-

-

-

-

-

-

-

409L

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

170

380

20

-

88

179

-

JIS

175

360

25

162

80

-

175

GB

170

380

20

-

88

179

200

410S

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

205

415

22

-

89

183

-

JIS

205

410

20

-

88

183

200

GB

205

415

20

-

89

183

200


Production Process and Feature

310S stainless steel round bar

310S stainless steel is austenitic chromium-nickel stainless steel with good oxidation resistance, corrosion resistance, because of the higher percentage of chromium and nickel, 310S has much better creep strength, continuous operation at high temperatures, with good The high-temperature resistance.

316L stainless steel round bar

cold-rolled products look good gloss, beautiful; due to the addition of Mo, corrosion resistance, especially excellent pitting corrosion resistance; Excellent high-temperature strength; excellent work hardening (weak magnetic processing)non-magnetic state of the solution;


316 stainless steel round bar

316 stainless steel is the second widely be used grade after 304, mainly for the food industry and surgical equipment, due to the addition of Mo, so its corrosion resistance, atmospheric corrosion resistance, and high-temperature strength is particularly good, Can be used in harsh conditions; excellent work hardening (non-magnetic).

321 stainless steel round bar

Add Ti element in 304 steel to prevent grain boundary corrosion, suitable for 430℃-900℃temperature use. In addition to the titanium added to reduce the risk of material corrosion of the weld other properties similar to 304

304L stainless steel round bar

304L stainless steel round bar is a low carbon content of 304 stainless steel variants, for welding occasions. The lower carbon content minimizes the precipitation of carbides in the heat affected zone adjacent to the weld, and the precipitation of carbides can cause stainless steel to cause intergranular corrosion (weld erosion) in some environments

304 stainless steel round bar

304 stainless steel is the most widely used chromium-nickel stainless steel, with good corrosion resistance, heat resistance, low-temperature strength and mechanical properties. Corrosion in the atmosphere, if it is an industrial atmosphere or heavily polluted areas, you need to be promptly cleaned to avoid corrosion.


Application

Mainly used for aircraft engine blades, casing, fasteners, combustion chamber, disk, shaft, combustion chamber wall, liquid oxygen kerosene engine, projectile, steam bottle, propulsion device. Widely used in aerospace, aviation, nuclear energy, nuclear energy, petroleum, chemical industry, and food, environmental protection, marine development, boiler heat exchanger and other fields.


We try our best to provide customers with more professional, standardized, international Free Samples 304 316 Stainless Steel Round Bar and services. We will promote the comprehensive, rapid and sustainable development of our company through innovation and continuous improvement of our management capabilities. Our company always adheres to the business philosophy of 'science and technology as the guide, marketing as the leader, quality as the center'.

Hot Tags: stainless steel round bar, China, manufacturers, suppliers, factory, wholesale, buy, price, disturbutor, for sale, stainless steel tube coil, Stainless Steel Stove Pipe, Stainless Sheet Metal, Stainless steel Tube, 316 stainless steel sheets, 430 stainless steel plate
Related Showrooms
Leave Message
Your privacy is important to us - we never sell or share your information.