Hot Rolled Stainless Steel Strip
The hot rolled all the necessity and stainless steel horizontal bar together for the loading, unloading and delivery car. So metal component factory prefers in case their machine is acceptable for strip generating efficiency and feeding to enhance the transporting buy steel strip.
Send InquiryProduct Description
Stainless steel strip be stored, delivery more convenience
The hot rolled all the necessity and stainless steel horizontal bar together for the loading, unloading and delivery car. So metal component factory prefers in case their machine is acceptable for strip generating efficiency and feeding to enhance the transporting buy steel strip.
Tax refund rate for stainless steel strip and stainless steel coil
China the width under 600mm is export for a strip Coil with tax refund that is 13%. There are just two ways In Be export after processing. The strip HS-CODE differs with coil the diameter point is 600mm.
Using tax refund that is 9%, but over or the diameter 600mm the item is export In The merchandise that's mean guarantee the coil that is bonded will Strip in place delivery to client is employ coil to 13% tax refund to export strip is to do the coil to exactly the slitting
Production Rang :
Thickness: 1.2mm - 10mm
Width: 30mm - 600mm, the wider products pls check in coil products
Finish: NO.1, 1D, #1, Hot rolled
Inner Diameter /ID: 508mm, 610mm
Main Grade ASTM-A240: 304 304L 304H 304DQ 316 316L 201 202 301 310s 430 410s 409 409L 444 4412205 2507 etc.
Main grade mechanical property in different standard
201 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 260 | 515 | 40 | - | 95 | 217 | - |
JIS | 275 | 520 | 40 | 241 | 100 | - | 253 |
GB | 205 | 515 | 30 | - | 99 | - | - |
202 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 260 | 620 | 40 | - | - | 241 | - |
JIS | 275 | 520 | 40 | - | 95 | 207 | 218 |
GB | - | - | - | - | - | - | - |
301 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 515 | 40 | - | 95 | 217 | - |
JIS | 205 | 520 | 40 | 207 | 95 | - | 218 |
GB | 205 | 515 | 40 | - | 95 | 217 | 218 |
304 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 515 | 40 | - | 92 | 201 | - |
JIS | 205 | 520 | 40 | 187 | 90 | - | 200 |
GB | 205 | 515 | 40 | - | 92 | 201 | 210 |
310S | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 515 | 40 | - | 95 | 217 | - |
JIS | 205 | 520 | 40 | 187 | 90 | - | 200 |
GB | 205 | 515 | 40 | - | 95 | 217 | 220 |
316L | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 170 | 485 | 40 | - | 95 | 217 | - |
JIS | 175 | 480 | 40 | 187 | 90 | 200 | |
GB | 170 | 485 | 40 | - | 95 | 217 | 220 |
409 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | - | - | - | - | - | - | - |
JIS | 175 | 360 | 22 | 162 | 80 | - | 175 |
GB | - | - | - | - | - | - | - |
409L | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 170 | 380 | 20 | - | 88 | 179 | - |
JIS | 175 | 360 | 25 | 162 | 80 | - | 175 |
GB | 170 | 380 | 20 | - | 88 | 179 | 200 |
410S | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 415 | 22 | - | 89 | 183 | - |
JIS | 205 | 410 | 20 | - | 88 | 183 | 200 |
GB | 205 | 415 | 20 | - | 89 | 183 | 200 |
430 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 450 | 22 | - | 89 | 183 | - |
JIS | 205 | 450 | 22 | 183 | 88 | - | 200 |
GB | 205 | 450 | 22 | - | 89 | 183 | 200 |
2205 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRC ≤ | HBW ≤ | HV ≤ |
ASTM | 450 | 655 | 25 | - | 31 | 293 | - |
JIS | - | - | - | - | - | - | - |
GB | 450 | 620 | 25 | - | 31 | 293 | - |
2507 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRC ≤ | HBW ≤ | HV ≤ |
ASTM | 550 | 795 | 15 | - | 32 | 310 | - |
JIS | - | - | - | - | - | - | - |
GB | 550 | 795 | 15 | - | 32 | 310 | - |
Production Process and Feature
Feature
Compare to cold rolled stainless steel strip, the hot rolled strip is thicker some, and hot rolled strip usually look like white without bright, but cold rolled a little bright.
Application
Use stainless steel strip to make higher efficiency for continuous punching line
Particularly when the strip will be continuous stamping as little metal parts to create higher efficiency Normally, the narrow flat steel is delivery as pub, but sometime as strip. Because by strip will create the feeding material price down compare to bar. When metal part is a litter long with flatness requirement the flat bar will be used.