Stainless Steel Wire for Spokes
Stainless steel spokes are among the critical components that influence the operation of spoke-style bikes and motorcycles. The most common problems that occur during usage are rust and breakage.
Send InquiryProduct Description
Stainless steel spokes are among the critical components that influence the operation of spoke-style bikes and motorcycles. The most common problems that occur during usage are rust and breakage. These issues not only affect the appearance, but also aren't conducive to the comfort and security of riding. .
The talked material is the decisive factor of talked performance. In recent decades, the talked material has slowly changed from conventional carbon steel to stainless steel. In comparison with carbon steel products, stainless steel products have clear benefits in terms of environmental protection, mechanical strength, corrosion resistance and appearance of the manufacturing procedure. At the moment, there are lots of manufacturers of stainless steel used for spokes at home and overseas, such as SUS304, lCrl8Ni9Ti, lCrl8Ni9Mo, 12Crl8Ni9, 06Crl8Mn3Ni8N, etc.. However, searching for stainless steel materials for blessings with greater functionality remains a research hotspot in the business.
Production Rang :
Size: Diameter 0.2mm-5.5mm, 5.5mm-12mm
Standard: GB1220, ASTM A 484/484M, EN 10060/ DIN 1013 ASTM A276, EN 10278, DIN 671
Main Grade: 201, 304, 316, 316L, 310s, 409, 430
Finish: Black, NO.1, mill finish, cold draw
Main grade mechanical property in different standard
201 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 260 | 515 | 40 | - | 95 | 217 | - |
JIS | 275 | 520 | 40 | 241 | 100 | - | 253 |
GB | 205 | 515 | 30 | - | 99 | - | - |
202 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 260 | 620 | 40 | - | - | 241 | - |
JIS | 275 | 520 | 40 | - | 95 | 207 | 218 |
GB | - | - | - | - | - | - | - |
304 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 515 | 40 | - | 92 | 201 | - |
JIS | 205 | 520 | 40 | 187 | 90 | - | 200 |
GB | 205 | 515 | 40 | - | 92 | 201 | 210 |
316L | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 170 | 485 | 40 | - | 95 | 217 | - |
JIS | 175 | 480 | 40 | 187 | 90 | 200 | |
GB | 170 | 485 | 40 | - | 95 | 217 | 220 |
409 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | - | - | - | - | - | - | - |
JIS | 175 | 360 | 22 | 162 | 80 | - | 175 |
GB | - | - | - | - | - | - | - |
310s | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 515 | 40 | - | 95 | 217 | - |
JIS | 205 | 520 | 40 | 187 | 90 | - | 200 |
GB | 205 | 515 | 40 | - | 95 | 217 | 220 |
410S | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 415 | 22 | - | 89 | 183 | - |
JIS | 205 | 410 | 20 | - | 88 | 183 | 200 |
GB | 205 | 415 | 20 | - | 89 | 183 | 200 |
Production Process and Feature
Innocent bright surface and stable mechanical properties.
Excellent anti-fatigue performance is the highlight.
The stainless steel wire for spokes has good surface quality and good mechanical properties. The tensile strength of Φ1.8-3mm merchandise is over 1200MPa, which is near or more than 1300MPa, which is significantly higher than that of stainless steel products of the same dimension. The results of bending fatigue evaluation and rust resistance Excellent performance, particularly suitable for bicycles and motorcycles.
Application
High-end bicycles, motorcycle spokes, main customers Giant, Merida, Xide Sheng, MACH 1.
The global market share is over 60%.