310s Stainless Steel Coil

310s Stainless Steel Coil Supplier

  • Thickness: 0.2mm – 200mm
  • Width: 300mm – 2000mm, the narrowed products pls check in strip products
  • Length: 500mm-12000mm
  • Finish: 2B, 2D, Black, NO.1, Anneal pickling
  • MOQ: 2MT

Product Description of 310s Stainless Steel Coil


310 stainless steel (national name: 0Cr25Ni20): Austenitic steel with great corrosion resistance, processability, and welding performance. Due to high nickel content and tissue that was steady, it’s generally treated by solution. High-temperature resistance. 310S stainless steel is austenitic chromium-nickel stainless steel that has good oxidation resistance, and corrosion resistance, since a greater proportion of nickel and chromium, have recoil strength and can continue working at elevated temperatures, with great immunity to High temperatures.

310s stainless steel coil manufacturer, 310s stainless steel coil suppliers

Because of the high content of nickel (Ni) and chromium (Cr), its good oxidation resistance, corrosion resistance, acid and alkali resistance, high-temperature resistance, high-temperature resistant steel pipe can be especially utilized in the production of electrical furnace tubes and other events, carbon in austenitic stainless steel After the material, because of the strong solution strengthening effect, the potency of the austenitic stainless steel relies on nickel, chromium, molybdenum, tungsten, tantalum, and titanium, due to its face-centered cubic construction.

Thus high strength and creep strength at elevated temperatures 310S stainless steel that is heat-resistant, is a version of 310 stainless steel. Domestic tier 0Cr25Ni20 tier 310S, also known as 2520, duplex stainless steel, for high-temperature furnace tube fabricating. 310S stainless steel pipe has good oxidation resistance and corrosion resistance, since a greater percentage of chromium and nickel, 310s has a recoil strength, can continue working at elevated temperatures, with good high-temperature resistance.

310S stainless steel maximum operating temperature of 1200 °C. Programs pipes, high-temperature furnace gallbladder microwave ovens, cremators, and other steels that require heat resistance, high heat/high-temperature contact parts.

High temperature resistant stainless steel, also referred to as 310S (0Cr25Ni20) stainless steel, is austenitic chromium-nickel stainless steel, has good oxidation resistance, and corrosion resistance, since a greater percentage of chromium and nickel, so it has much better creep strength, Can continue to work at elevated temperatures, with good high-temperature resistance.

Due to the high content of nickel (Ni) and chromium (Cr), its good oxidation resistance, corrosion resistance, acid and alkali resistance, higher temperature resistance, high-temperature resistant steel is specially used in the creation of electric furnace tubes and other events, carbon in austenitic stainless steel After the content, because of the solid solution strengthening result, the strength of the austenitic stainless steel is inserted into the chromium, nickel-based molybdenum, tungsten, tantalum, and titanium, owing to its face-centered cubic structure.

For that reason, it has high strength and creeps strength at high temperatures.

Production Range of 310s Stainless Steel Coil:


-310s Cold Rolled Stainless Steel coil, Cold rolled 310s coil, 310s CRC.

  • · Thickness: 0.2mm – 8.0mm
  • · Width: 600mm – 2000mm, the narrowed products pls check in strip products
  • · Max coil weight: 25MT
  • · Coil ID: 508mm, 610mm
  • · Finish: 2B

-310s Hot Rolled Stainless Steel coil, Hot Rolled 310s coil, 310s HRC.

  • · Thickness: 1.2mm – 16mm
  • · Width: 600mm – 2000mm, the narrower products please check in strip products
  • · Max coil weight: 40MT
  • · Coil ID: 508mm, 610mm
  • · Finish: NO.1

310s Grade description in different standard

ISO Name

ASTM

DIN / EN

JIS

GB

Other

X12CrNi23-12

S31008

310S

1.4951

SUS310S

S31008

06Cr25Ni20 0Cr25Ni20

310s Grade Chemical components in different standard

310s

C %

Si %

Mn %

P %

S %

Ni %

Cr %

Mo %

N %

Cu %

ASTM

0.08

1.50

2.00

0.045

0.030

19.0-22.0

24.0-26.0

DIN/EN

0,10

1,50

2,00

0,045

0,015

19,0-22,0

24,0-26,0

0,10

JIS

0.08

1.50

2.00

0.045

0.030

19.0-22.0

24.0-26.0

GB

0.08

1.50

2.00

0.045

0.030

19.0-22.0

24.0-26.0

310s mechanical property in different standard

310s

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

205

515

40

95

217

JIS

205

520

40

187

90

200

GB

205

515

40

95

217

220

Production Process and Feature


310 stainless steel (domestic name: 0Cr25Ni20): Austenitic steel with great corrosion resistance, processability, and welding operation. As a result of high nickel content and stable tissue, a strong solution generally treats it.

310S stainless steel is chromium-nickel steel that has good oxidation resistance because a greater percentage of chromium and nickel, has a far superior creep strength, and can keep on functioning at high temperatures, with a resistance temperature that is High.

Because of the high content of nickel (Ni) and chromium (Cr), its good chemical resistance, corrosion resistance, acid and alkali resistance, high-temperature resistance, high-temperature resistant steel pipe is especially utilized in the creation of electric furnace tubes and other events, carbon in austenitic stainless steel After the material, due to its solid solution strengthening result, the potency of the austenitic stainless steel relies on nickel, chromium, molybdenum, tungsten, tantalum, and titanium, owing to its face-centered cubic construction.

Thus Higher strength and creep strength at elevated temperatures 310S stainless steel, is a variant of 310 stainless steel, S for specific purposes. American tier 310S, grade 0Cr25Ni20, also known as 2520, duplex stainless steel, for high-temperature furnace tube manufacturing. 310S stainless steel pipe has corrosion resistance and good oxidation resistance, since a greater proportion of chromium and nickel, 310s include a much superior creep strength, and can keep on working at high temperatures, together with good high-temperature resistance. 310S stainless steel maximum operating temperature of 1200 °C.

Programs: Exhaust pipes, high-temperature furnace gallbladder microwave ovens, cremators and steels that require heat resistance, higher heat/high-temperature contact parts. High temperature resistant stainless steel, also referred to as 310S (0Cr25Ni20) stainless steel, is austenitic chromium-nickel stainless steel, has good oxidation resistance, and corrosion resistance, since a higher proportion of nickel and chromium, so it has better creep strength, Can continue working at elevated temperatures, with good high-temperature resistance.

Because of the high content of nickel (Ni) and chromium (Cr), it has good chemical resistance, corrosion resistance, acid and alkali resistance, and higher temperature resistance, high-temperature resistant steel is especially used in the creation of electrical furnace tubes and other occasions, carbon in austenitic stainless steel Subsequent to the content, because of its strong solution strengthening effect, the strength of the austenitic stainless steel has been added to the chromium, nickel-based molybdenum, tungsten, tantalum, and titanium, due to its face-centered cubic structure.

Therefore, it has high strength and creeps strength at high temperatures.

Corrosion resistance

The 310S can be used with between 15% and 50% sulfuric acid. (Due to its high heat resistance in high-temperature environments, material properties will not decrease

Heat resistance, Wear resistance

Because 310S has a higher melting point than 316L, it is more wearable than 316L in high-temperature, high-speed friction environments.

Application


Products wrapped, could be forced into a tube. Steam turbines, Boilers, industrial furnaces and air travel, petrochemical, and other elements of the components at high temperatures.

Utilized in the manufacture of steam The substance that was 310/310s is utilized as sexy Standing for the business program there are a number of 310/310s