316L 316 Stainless Steel Coil

316 316L Stainless Steel Coil Supplier

  • Thickness: 0.2mm – 200mm
  • Width: 300mm – 2000mm, the narrowed products pls check in strip products
  • Length: 500mm-12000mm
  • Finish: 2B, 2D, Black, NO.1, Anneal pickling
  • MOQ: 2MT

Product Description


316L is steel. Due to the molybdenum content in the steel, the 316L stainless steel’s overall functioning is better than that of 304 and 310 stainless steel. 316L stainless steel also has good resistance to chloride erosion, it is usually used for the marine environment.

After welding. 316 is 316L Applications that must not be annealed and require maximum corrosion resistance A stainless steel, to corrosion resistance as a result of the inclusion of Mo components, and high-temperature strength has improved temperature as much as 1200-1300 degrees, can be used under harsh circumstances.

Production Range :


-316 316L Cold Rolled Stainless Steel coil, Cold rolled 316 316L coil, 316 316L CRC.

  • · Thickness: 0.2mm – 8.0mm
  • · Width: 600mm – 2000mm, the narrowed products pls check in strip products
  • · Max coil weight: 25MT
  • · Coil ID: 508mm, 610mm
  • · Finish: 2B

-316 316L Hot Rolled Stainless Steel coil, Hot Rolled 316 316L coil316 316L HRC.

  • · Thickness: 1.2mm – 16mm
  • · Width: 600mm – 2000mm, the narrower products please check in strip products
  • · Max coil weight: 40MT
  • · Coil ID: 508mm, 610mm
  • · Finish: NO.1

316 mechanical property in different standard

316

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

205

515

40

95

217

JIS

205

520

40

187

90

200

GB

205

515

40

95

217

220

316L mechanical property in different standard

316L

Y.S./Mpa ≥

T.S./Mpa ≥

E.L./% ≥

HB ≤

HRB ≤

HBW ≤

HV ≤

ASTM

170

485

40

95

217

JIS

175

480

40

187

90

 

200

GB

170

485

40

95

217

220

Production Process and Feature


Corrosion resistance

atmosphere. The production process has good corrosion resistance. And 316 stainless steel is Corrosion 316 Corrosion resistance is Far Better than 304 stainless steel, in the paper and pulp Resistant to the erosion of the oceans and the industrial Resistance is better than 304 stainless steel, with good corrosion resistance in the production process of paper and pulp. Moreover, 316L stainless steel is also resistant to erosion by marine and competitive industrial atmospheres.

Heat resistance

It’s wise to not always use 316 stainless steel in the range of 427 ° C-857 ° C (800 ° F-1575 ° F), but stainless steel possesses exceptional heat resistance if 316 stainless steel is continuously used outside this temperature range. 316L stainless steel carbide precipitation functionality better than 316 stainless steel. 316L stainless steel has good oxidation resistance in irregular use below use that is constant and 1600 °C below 700 °C. In the range of 800-1575 levels, it’s advisable to not continue to act. 316L stainless steel, but if 316L stainless steel is used outside this temperature range, stainless steel has good heat resistance. 316L stainless steel has better precipitation resistance than stainless steel and may be used in the temperature range that is above.

Heat treatment

The alternative annealing is done at a temperature assortment of 1010-1150 levels and then cooled. 316L stainless steel can’t be hardened by heat treatment. Annealing is done in a temperature in the assortment of 850-1050 ° C followed by annealing. Stainless steel can’t be hardened by heat treatment.

Welding performance

316 stainless steel. All welding procedures may be used for welding. Welding may be utilized in line with 309Cb steel filler sticks, respectively 316Cb, 316L or this function or welding electrodes. To be able to acquire the best corrosion resistance, the stainless steel section has to be annealed after welding. No annealing is needed In case 316L stainless steel is utilized. All welding procedures may be used for welding. After welding, 309Cb steel filler sticks, 316L or 316Cb or welding rods may be used in line with this program. For resistance, annealing is required by the segment of stainless steel. Post-weld annealing isn’t required In case 316L stainless steel is utilized.

Application


The main uses are paper and papermaking equipment, heat exchangers, dyeing equipment, film processing equipment, pipelines, construction exterior materials in coastal areas. Used within the business of valves, housings, clamps, ball, valve body, seat, nut, stem and so on. Pulp and paper gear heat exchangers, dyeing equipment, film processing equipment, pipes, exterior materials for buildings in coastal regions, and watch chains, watch cases as well as applications of high-level watches. Seawater with equipment, substances, dyes, paper acid, fertilizer and manufacturing equipment; camera, food industry staples, CD poles, bolts, nuts.