Embossed Stainless Steel Sheets
Embossing means making some sorts of patterns, impressions or layouts onto a different surface such as fabric, paper, metal or leather. Stainless steel sheets are employed in several fields in high traffic locations and have been made from metal.
Send InquiryProduct Description
Embossing means making some sorts of patterns, impressions or layouts onto a different surface such as fabric, paper, metal or leather. Stainless steel sheets are employed in several fields in high traffic locations and have been made from metal. Those sheets' manufacturing process entails rolling of patterns that are unique to the sheets. A number of the patterns which you could search to get are wood grain sawn cedar, leather grain, weather grain, along with stucco.
Production Rang :
Main Grade: 304, 201, 430,
Thickness: 0.3mm - 4.0mm
Width: 1000/1219/1500mm/customized
Length: 6000mm/coil
Film: Double PE/laser PE
Pattern: Leather 2B Mill Finish stainless steel,
Leather Rose Gold stainless steel,
Leather BA stainless steel,
Wood Brass stainless steel,
Linen BA stainless steel,
Linen Antique stainless steel,
Linen Brass stainless steel,
ICY Bamboo stainless steel,
Square embossed stainless steel,
6WL stainless steel,
5WL stainless steel
Main grade description in different standard
ASTM | DIN / EN | JIS | GB | ISO Name | Other |
S20100 201 | 1.4372 | SUS201 | S35350 | X12CrMnNiN17–7-5 | J1 L1 LH 201J1 |
S20200 202 | 1.4373 | SUS202 | S35450 | X12CrMnNiN18–9-5 | 202 L4, 202 J4, 202 J3 |
S30400 304 | 1.4301 | SUS304 | S30408 | X5CrNi18-10 | 06Cr19Ni10 0Cr18Ni9 |
S31603 316L | 1.4404 | SUS316L | S31603 | X2CrNiMo17-12-2 | 022Cr17Ni12Mo2 00Cr17Ni14Mo2 |
S40900 409 | - | SUH409 | S11168 | X5CrTi12 | 0Cr11Ti |
S40910 409L | 1.4512 | SUH409L | S11163 | X2CrTi12 | 00Cr11Ti 022Cr11Ti |
S41008 410S | 1.4000 | SUS410S | S11306 | X6Cr13 | - |
S43000 430 | 1.4016 | SUS430 | 10Cr17 | X6Cr17 | 1Cr17 |
Main grade chemical component in different standard
201 | C % | Si% | Mn % | P % | S % | Ni % | Cr % | N % | Mo % |
ASTM | 0.15 | 1.00 | 5.5-7.5 | 0.050 | 0.030 | 3.5-5.5 | 16.0-18.0 | 0.25 | - |
DIN/EN | 0,15 | 1,00 | 5,5-7,5 | 0,045 | 0,015 | 3,5-5,5 | 16,0-18,0 | 0,05-0,25 | - |
JIS | 0.15 | 1.00 | 5.5-7.5 | 0.060 | 0.030 | 3.5-5.5 | 16.0-18.0 | 0.25 | - |
GB | 0.15 | 1.00 | 5.5-7.5 | 0.050 | 0.030 | 3.5-5.5 | 16.0-18.0 | 0.05-0.25 | - |
202 | C % | Si% | Mn % | P % | S % | Ni % | Cr % | N % | Mo % |
ASTM | 0.15 | 1.00 | 7.5-10.0 | 0.060 | 0.030 | 4.0-6.0 | 17.0-19.0 | 0.25 | - |
DIN/EN | 0,15 | 1,00 | 7,5-10,5 | 0,045 | 0,015 | 4,0-6,0 | 17,0-19,0 | 0,05-0,25 | - |
JIS | 0.15 | 1.00 | 7.5-10.0 | 0.060 | 0.030 | 4.0-6.0 | 17.0-19.0 | 0.25 | - |
GB | 0.15 | 1.00 | 7.5-10.0 | 0.050 | 0.030 | 4.0-6.0 | 17.0-19.0 | 0.05-0.25 | - |
304 | C % | Si% | Mn % | P % | S % | Ni % | Cr % | N % | Mo % |
ASTM | 0.08 | 0.75 | 2.00 | 0.045 | 0.030 | 8.0 - 10.5 | 18.0-20.0 | 0.10 | - |
DIN/EN | 0,07 | 1,00 | 2,00 | 0,045 | 0,015 | 8,0 - 10,5 | 17,5-19,5 | 0,10 | - |
JIS | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 8.0 - 10.5 | 18.0-20.0 | - | - |
GB | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 8.0 - 10.0 | 18.0-20. 0 | - | - |
316L | C % | Si% | Mn % | P % | S % | Ni % | Cr % | N % | Mo % |
ASTM | 0.030 | 0.75 | 2.00 | 0.045 | 0.030 | 10.0-14.0 | 16.0-18.0 | 0.10 | 2.00-3.00 |
DIN/EN | 0,030 | 1,00 | 2,00 | 0,045 | 0,015 | 10,0-13,0 | 16,5-18,5 | 0,10 | 2,00-2,50 |
JIS | 0.030 | 1.00 | 2.00 | 0.045 | 0.030 | 12.0-15.0 | 16.0-18.0 | - | 2.00-3.00 |
GB | 0.030 | 0.75 | 2.00 | 0.045 | 0.030 | 10.0-14.0 | 16.0-18.0 | 0.10 | 2.00-3.00 |
409 | C % | Si% | Mn % | P % | S % | Ni % | Cr % | N % | Ti % |
ASTM | 0.08 | 1.00 | 1.00 | 0.045 | 0.03 | 0.50 | 10.5-11.7 | - | 6*C% - 0.75 |
DIN/EN | - | - | - | - | - | - | - | - | - |
JIS | 0.08 | 1.00 | 1.00 | 0.040 | 0.030 | - | 10.5-11.7 | - | 6*C% - 0.75 |
GB | 0.08 | 1.00 | 1.00 | 0.045 | 0.030 | 0.60 | 10.5-11.7 | - | 6*C% - 0.75 |
409L | C % | Si% | Mn % | P % | S % | Ni % | Cr % | N % | Ti % |
ASTM | 0.03 | 1.00 | 1.00 | 0.040 | 0.020 | 0.50 | 10.5-11.7 | 0.03 | 6*(C+N)-0.5 |
DIN/EN | 0.03 | 1.00 | 1.00 | 0.040 | 0.015 | - | 10.5-12.5 | - | 6*(C+N)-0.65 |
JIS | 0.03 | 1.00 | 1.00 | 0.040 | 0.030 | - | 10.5-11.7 | - | 6*C% - 0.75 |
GB | 0.03 | 1.00 | 1.00 | 0.040 | 0.020 | - | 10.5-11.7 | 0.03 | Ti≥8*(C+N) |
410S | C % | Si% | Mn % | P % | S % | Ni % | Cr % | N % | Mo % |
ASTM | 0.08 | 1.00 | 1.00 | 0.040 | 0.030 | 0.60 | 11.5-13.5 | - | - |
DIN/EN | 0,08 | 1,00 | 1,00 | 0,040 | 0,015 | - | 12,0-14,0 | - | - |
JIS | 0.08 | 1.00 | 1.00 | 0.040 | 0.030 | - | 11.5-13.5 | - | - |
GB | 0.08 | 1.00 | 1.00 | 0.040 | 0.030 | 0.60 | 11.5-13.5 | - | - |
Main grade mechanical property in different standard
201 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 260 | 515 | 40 | - | 95 | 217 | - |
JIS | 275 | 520 | 40 | 241 | 100 | - | 253 |
GB | 205 | 515 | 30 | - | 99 | - | - |
202 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 260 | 620 | 40 | - | - | 241 | - |
JIS | 275 | 520 | 40 | - | 95 | 207 | 218 |
GB | - | - | - | - | - | - | - |
304 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 515 | 40 | - | 92 | 201 | - |
JIS | 205 | 520 | 40 | 187 | 90 | - | 200 |
GB | 205 | 515 | 40 | - | 92 | 201 | 210 |
316L | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 170 | 485 | 40 | - | 95 | 217 | - |
JIS | 175 | 480 | 40 | 187 | 90 | 200 | |
GB | 170 | 485 | 40 | - | 95 | 217 | 220 |
409 | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | - | - | - | - | - | - | - |
JIS | 175 | 360 | 22 | 162 | 80 | - | 175 |
GB | - | - | - | - | - | - | - |
409L | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 170 | 380 | 20 | - | 88 | 179 | - |
JIS | 175 | 360 | 25 | 162 | 80 | - | 175 |
GB | 170 | 380 | 20 | - | 88 | 179 | 200 |
410S | Y.S./Mpa ≥ | T.S./Mpa ≥ | E.L./% ≥ | HB ≤ | HRB ≤ | HBW ≤ | HV ≤ |
ASTM | 205 | 415 | 22 | - | 89 | 183 | - |
JIS | 205 | 410 | 20 | - | 88 | 183 | 200 |
GB | 205 | 415 | 20 | - | 89 | 183 | 200 |
Production Process and Feature
Embossed stainless steel sheets
Undergo an extremely rigorous procedure to boost their quality and endurance. The manufacturing principle is to create a design that may last long in extreme and hazardous environments. The embossing system allows rolling of text, published numbers or perhaps symbols on pipes, cables and other equipment. Build successful dispersion of the lubricants the secret of the manufacturing Procedure is to create friction, Enhance metal sheet rigidity and stiffness, and ascension a metal surface area for heat transfer or acoustic applications, and boost grip
Embossed sheet metal Material:
Embossed steel sheets are created with steel. A number of the substances are mild steel aluminum, or stainless steel. The material needs to have endurance traits, capable to endure medium and capability to keep the depth during the procedure. The most significant thing you need to remember is the caliber is finished. Ensure the alloy is of the quality that is premium and doesn't alter its shape.
Application
In a diverse range of fields sheets are used On the current market. On the other hand, the key applications of these sheets are practical and aesthetic. Some of the notable applications are automotive trim, elevator panels, garage door panels, metal office furniture, stair tread, and building solutions.